Processing case Analysis
Processing part name: gear Hardness: Hrc58-62
Materials:Gcr15 ap=0.1mm Vc=150m/min f=0.12mm/r Processing style：Dry
Inserts type:CNGN120408/CCGW09T304 Grade:BCN4700
Processing part name：Lathe bed Hardness:HB200-300 Materials：cast iron ap=0.1~1mm Vc=600~800m/min f=0.1-0.15mm/z Style：Dry Inserts type:SNFN120412
Grade:BCN3700

Processing part name:Engine Hardness:HB200-300 Materials: cast iron ap=0.1~1mm Vc=600~800m/min f=0.1-0.15mm/z
Style：Dry Inserts type:SNFN120412
Grade:SBN4700

Processing case Analysis
Processing part name:Slurry pump Hardness:HRC60 Materials:High chromium cast iron ap=0.5~4mm Vc=50~90m/min f=0.1~0.5mm/r Style：Dry Inserts type:SNGN1608
Grade:BCN5700/4700
Processing part name:Mould Hardness:HRC50~62 Materials:Tool steel ap=0.5mm Vc=150m/min f=0.1~0.2mm/r Style: Dry Inserts type:CNGN120412
Grade:BCN4700
Processing part name:Steel bushing Hardness:HRC58-62 Materials:Gcr15 ap=0.1mm
Vc=150m/min f=0.12mm/r Style：Dry Inserts type:CNGN120408/CCGW09T304
Grade:BCN3700/BCB3700
Processing case Analysis
Processing part name:Abrasive plate Hardness:HRC52-62 Materials:Gr15 ap=3~4mm Vc=150m/min f=0.1mm/r Style：Dry Inserts type:SNGN1206
Grade:BCN4700
Processing part name: Auto parts Hardness:HB180 Materials:QT200~300 ap=2~3mm Vc=450~600m/min f=0.35~0.6mm/r Style:Dry
Inserts type:CNGN120412
Grade:BCN4700

Processing part name:The shaft Hardness:HRC60 Materials:Gr15 ap=0.5~2mm Vc=150m/min f=0.25mm/r Style：Dry Inserts type:SNGN1204
Grade:BCN2700